Claus Catalyst

Item No.: EniSorb 102A 102B 102C 111
Size: 2-3mm 3-4mm 4-6mm
Application: Sulfur Recovery Claus Catalyst
  • Size: 2-5mm 3-4mm 4-6mm
  • Surface Area: 250-330m2/g
  • Crushing Strength: 80-200N/PC
  • Bulk Density: 0.70-0.80g/ml
  • Package: 25kg/bag, 150kg/steel drum, 750-1000kg/supersack
  • MOQ: 750kg
  • Sample: 0.5-25kg
  • Description
    Gophin Chemical provides the catalyst used for sulfur recovery process in the Claus production process. Our catalyst can solve the problems of surface area decreasing, activity decreasing, and service life shortening of Claus catalyst.

    EniSorb-102A claus catalyst activated alumina applied in the sulfur recovery process is mainly used to catalyze the claus sulfur recovery technique in which H2S reacts with SO2 to generate pure sulfur.

    EniSorb-102B Because the existing of trace oxygen and organic sulfur in the feed gas will generate sulfate at the working conditions of claus device, the widely used activated alumina sulfur recovery catalyst has obvious disadvantages, that is BET decreasing and activity loss.

    EniSorb-111 claus catalyst activated alumina for Iron oxide sulfur recovery is a high-activity deoxidized catalyst. It mainly consists of activated alumina and activated metal salts. By using this catalyst, the O2 concentration can be decreased to under 10ppm, and the alumina catalyst can avoid acidification.

     
    Product EniSorb Activated Alumina Claus Catalyst
    Type A102A A102B A102C A111
    Application Claus sulfur recovery catalyst Claus sulfur recovery catalyst CuO desulfurizer catalyst Iron sulfur recovery catalyst
    Sphere Size (mm) 4~6 4~6 2~4, 3~5 4~6
    Appearance White Sphere White Sphere Grey Sphere Brown Sphere
    Surface Area (m2/g) 330 240 250~300 280
    Bulk Density (g/cm3) 0.70~0.80 0.70~0.80 0.70~0.80 0.70~0.80
    Abrasion Loss (%) 0.1 0.1 0.1 0.1
    Pore Volume (cm3/g) 0.45~0.50 0.45 0.45~0.50 0.45
    Crushing Strength (N/pc) 200 200 80~120 200
    Al2O3 (%) 94% 88 95 88
    Na2O (%) 0.25% -- -- --
    CuO (%) -- -- 5.0 --
    Fe2O3 (%) -- -- -- 6
    TiO2 (%) -- 5.0 -- --
    Package 25kg/bag, 150kg/steel drum, 750kg/supersack.